JSC «Volzhsky Abrasive Works»
CUMI-Murugappa Group
Metallurgical fractions
Metallurgical fractions
| № | Description of fraction | Particle size distribution | Chemical composition |
|---|---|---|---|
| 1. | SiC 92-94% 0-15 mm |
+15 mm – 10% max -0,5 mm – 50% max |
SiC – 92%min |
| 2. | SiC 92-94% 0-10 mm |
+10 mm – 10% max -0,5 mm – 50% max |
SiC – 92% min |
| 3 | SiC 92-94% 0-1,6 mm |
0–1,6mm – 85 % min +1,6 mm – 10 % max |
SiC – 92%min |
| 4. | SiC 92-94% 1,6 - 10 mm |
1,6–10 mm – 85 % min - 1,6 mm – 10 % max |
SiC – 92%min |
| 5. | SiC 92-94% 1-3 mm |
+3,35 mm – 10% max -1,0 mm – 10% max |
SiC – 92% min Fe – 2% max C – 2-5% Siсв. – 3-5% |
| 6. | SiC 92-94% 0-1 mm |
+1,0 mm – 10% max | SiC – 92% min Fe – 2% max C – 2-5% Siсв. – 3-5% |
| 7. | SiC 93% 0 – 0,07 mm 220 F |
+0,075 mm - 10%max -0,045 mm - 35-90% min |
SiC – 93 % min С - 0,5% max |
| 8. | SiC 92 % 325 F |
+0,075 mm – 5% max -0,045 mm –80% min |
SiC – 92 % min Fe – 1,2 % max C – 0,5 % max |
| 9. | SiC 90% -3,35+0,3 mm |
+3,35 mm – 5% max -0,3 mm –10% max |
SiC – 90% min Fe – 5% max |
| 10. | SiC 90% 0-0,3 mm |
+0,3 mm – 10% max | SiC – 90% min Fe – 5% max |
| 11. | SiC 90% -3,35+0,212 mm |
+3,35 mm – 5% max -0,212 mm –10% max |
SiC – 90% min Fe – 5% max |
| 12. | SiC 90% 0-0,212 mm |
+0,212 mm – 10% max | SiC – 90% min Fe – 5% max |
| 13. | SiC 88% 0-10 mm |
+10 mm – 10% max -0,5 mm – 50% max |
SiC – 88% min |
| 14. | SiC 88% 0-15 mm |
+10 mm – 10% max -0,5 mm – 50% max |
SiC – 88% min |
All technical properties can be adjusted in accordance with requirments and wishes of customers.